8406-20G 8406 WICKING GRADE ADHESIVE LOW VISCOSITY 20ML

DESCRIPTION

20ML CHEMTOOLS 8406 CYANOACRYLATE ADHESIVE - LOW VISCOSITY, FAST CURE SPEED

Instant Adhesive 8406

Cyanocrylate adhesives offer a major advantage over other types of adhesive systems. They are a single componentadhesive, fast curing at room temperature, solvent free and resistant to many environmental factors.

FEATURES:

CHEMTOOLS 8406 is low viscosity combined with fast curespeed, surface insensitive cyanoacrylate adhesive (CA). It is specifically formulated to bond difficult surfaces with high industrial strength..

Ideal for bonding rough, porous and acidic surfaces including Wood, Cardboard, Balsa Wood, Rubbers, Plastics, Metals, Leather, etc.

Wide variety of industrial manufacturing and repairingapplications

Meets Military specification MLLA 46050 Type II Class II

One part adhesive
Solvent free
Fast curing at room temperature
High Tensile shear strength
Surpasses most other types of adhesives for bonding rubbers.

APPLICATIONS:

Ideal for bonding rough, porous and acidic surfaces including Wood, Cardboard, Balsa Wood, Rubbers, Plastics, Metals, Leather, etc.
Wide variety of industrial manufacturing and repairing applications

BONDING TIMES:

Plastics 2-5 seconds
Rubbers
Wood 1-5 seconds
Leather 5-15 seconds
Metals 8-10 seconds
Ceramics 12-18 seconds

PHYSICAL PROPERTIES:

Liquid
Composition Ethyl Cyanoacrylate
Appearance Colorless liquid
Viscosity@ 25°C 20 cps
Brookfield LVT Spindle 1@ 30 rpm
Cured Adhesive
Gap Filling 0.05mm
Tensile Shear Strength 18-28 n/mm2
Service Temperature Range -60 to 80ºC
Full Cure 24 hours
Melting Point Temperature 160 to 170ºC

Shear Strength ASTM D 1002/DIN 53283

Grit Blasted Steel >20 N/mm2
Etched Aluminum >18 N/mm2
Rubbers >22 N/mm2
Wood >25 N/mm2
Polycarbonate >12 N/mm2
ABS >10 N/mm2

Mechanical Properties:

Coefficient of thermal conductivity, ASTM C177, W.m-1 k-1 0.1
Glass Transition Temperature, ASTM E228, 122ºC
Coefficient of thermal expansion, ASTM D696, K-1 75x 10-6
Dielectric strength, ASTM D149, kV/mm 27
Volume resistivity, ASTM D257, Ohm.cm 1 x 1016
Dielectric constant, 25 ºC, ASTM D150 2.7

APPLICATION INSTRUCTIONS

All surfaces must be clean, dry, dust and grease free. Best result will be achieved with surfaces that have been lightly abraded immediately prior to bonding.
If using accelerator apply to one component surfaceonly. Apply thin film of adhesive to the other surface and bring the pieces together immediately. Hold for few seconds without disturbing the joints.
When bonding “O” rings, cut a fresh surface onto each end of the rubber to gain the best possible strength.

Weight: 0.0320 kg